NEster

polyester resin for hybrid power coating

Principal Properties and Applications
NEster® P 5010 is a medium reactivity polyester resin, designed for
50/50 epoxy/polyester hybrid system. Powder coatings based on it
exhibit good flow and excellent overbake resistance.
Product Specifications
Property		Range	Test Method
Appearance		Pale granules	Visual
Acid value, mgKOH/g		66~76	ASTM D1639
Viscosity @ 175°C, mPa·s		7000~11000	ASTM D4287
Gardner Color(50% solution)		max.3	ASTM D1544
Other Data
Property		Range	Test Method
Glass transition temp., °C		approx. 55	DSC
Packaging
White PE bag, N.W.25kg/bag, 1000kg/pallet.
Storage
The product can be stably stored for at least one year when kept
in closed containers in a dry and clean place at temperature below
30°C. For product older than one year, it is recommended to confirm
by testing prior to use. Exposure to sunlight should be avoided.

Starting Formulation
Component		Weight %
NEster® P 5010		32.0
Epoxy Resin1)		32.0
Titanium dioxide2)		34.5
Flow control agent3)		1.0
Benzoin		0.5
1)DER 663U Dow Chemicals, or Araldite GT 7004, Huntsman
2) Ti-Pure® R-706, DuPont, or Kronos 2310 Kronos Titanium
3) Resiflow PV5, Worlée-Chemie, or BYK 365P BYK-Chemie
Extrusion & Application Conditions
Extruder:	SLJ-30A
Zone I temp.:	85~105°C
Zone II temp.:	100~120°C
Screw speed:	200rpm
Panel:	0.5mm pre-treated cold-rolled steel
Spray gun:	Corona spray gun
Voltage:	60~90kV
Curing conditions:	15 min. @ 180°C
Film Properties
Property		Result	Test Method
Film thickness, μm		approx. 60	ASTM D1186
Gloss @ 60º, %		min. 90	ASTM D523
Direct/reverse impact, inch lbs		160/160	ASTM D2794
1/8" Conical mandrel		pass	ASTM D522
Adhesion(cross cut)		5B	ASTM D3359
Pencil hardness(Mar)		H	ISO 15184-98